HOT WORKING TOOLS STEELS
| Quality |
DIN |
No. |
| Hot Working Tools Steels |
X 40 CrMoV 5 1 |
WN 1.2344 |
|
|
| C |
Cr |
Mo |
V |
Si |
| %0.39 |
%5.0 |
%1.3 |
%1.0 |
%1.1 |
|
Chemical analysis
| C | Si | Mn | Cr | Mo | V |
| 0,40 % | 1,00 % | 0,40 % | 5,0 % | 1,3 % | 1,0 % |
|
|
Heat treatment:
| Soft annealing: | 750 – 800 °C | Oil |
| Hardening: | 1020 – 1080 °C | Oil |
| Tempering: | °C | 100 | 200 | 300 | 400 | 500 | 600 |
| (three times) | HRC | 53 | 52 | 52 | 54 | 56 | 50 |
|
| Quality |
DIN |
No. |
| Hot Working Tools Steels |
X 32 CrMoV 3 3 |
WN 1.2365 |
|
|
| C |
Cr |
Mo |
V |
| %0.31 |
%2,9 |
%2,8 |
%0,5 |
|
| Quality |
DIN |
No. |
| Hot Working Tools Steels |
56 NiCrMoV 7 |
WN 1.2714 |
|
|
| C |
Cr |
Mo |
Ni |
V |
| %0,55 |
%1,1 |
%0,5 |
%1,7 |
%0,1 |
|
|
High Temperature
strength |
High temperature
toughness |
High temperature
wear resistance |
Machinability |
DIN |
AISI |
| ArW 2344 |
 |
|
|
|
WN 1.2344 |
H13 |
| ArW 2343 |
|
|
|
|
WN 1.2343 |
H11 |
| ArW 2365 |
|
|
|
|
WN 1.2365 |
H10 |
| ArW 2714 |
|
|
|
|
WN 1.2314 |
-- |
|
|